Mangalam Industrial Products was established by Mr. Yashwant Upadhyay in the year 1988 as a trading company dealing in Electronic components like Wire Wound Resistors, Electrolytic capacitors, Thick film Metal Oxide resistors, LED indicating modules, Wire Wound Potentiometers, High Alumina Ceramic textile thread guides, Pump seal faces and Electrical / Thermal application insulating components.
Ceramic Insulating Components needed by Electrical and Thermal applications has a very vast potential market for quality products and hence started developing customers and supply resources. In process started getting products made as per customer's specifications and applications. Having associated with different product groups, started manufacturing specialized components of porcelains and ceramics, besides continuing association with selected approved manufacturing units. All Associate units have all the facilities from tool making to finished products. Customers are OEMs, Exporters and Traders.
STEATITE - C221
- Basically magnesium silicate
- Impervious material structure
- Very good Mechanical Strength
- High volume resistivity upto 1000 degree C.
- Low dissipation factor
- Good dielectric strength
- Very popular
- Beads are used for insulation of wire where, plastic coating can not be used.
- MCB Plates are used in MCB to prevent arc from reaching plastic body.
- Cartridge Heaters and End Seals are used at the end portion of Thermocouple or Heaters as Insulator.
- Band Heaters are used in covering heating coil in Band Heaters.
- Thermostat and Lamp Holders are made out of C-221 Steatite and basically are Insulators.
LOW VOLTAGE INSULATORS
PORCELAIN - C112
- Basically Alkaline Alumina Silicate
- Economic Insulator.
- Good Mechanical Strength
- Good resistance to chemical attack
- Widely popular
Mainly these types of Insulators are used in re-wirable type of Fuse units and where the application is upto 2.5 KVA.
CORDIERITE REFRACTORY C-511
Properties \ Material |
Unit |
|
|
Equivalent to DIN EN 60672 |
|
C-511 |
Main Ingredients\Composition |
SiO 2%
Al2O 3%
MgO % |
50
35
10 |
Physical Properties |
Colour |
|
Brown |
Specific Gravity |
|
1.9 |
Water Absorption |
% |
20 |
Flexural Strength |
kg/cm2 |
250 |
Compressive Strength |
kg/cm2 |
1200 |
Young's Modulus |
kg/cm2 x 106 |
- |
Hardness |
Moh's |
- |
Thermal Properties |
Co-efficient of Thermal Expansion
(30-600 degree Celsius) |
10-6/°K |
4 - 6 |
Thermal Shock Resistance Down Shock  T |
°C |
350 |
Thermal Conductivity |
W / M°K |
1.3 - 1.8 |
Max. Temp. Withstanding Capacity |
°C |
1100 |
Electrical Properties |
Dielectric Strength (20C) |
KV / mm |
- |
Dielectric Constant (20C : : 1MHz) |
|
- |
Volume Resistivity (20C) |
Ohm-cm |
- |
| Application |
| Bobbins/Multi Hole Tubes. |